Developments, characterization and proton irradiation damage tests of AlN detectors for VUV solar observations

BenMoussa A., Soltani A., Gerbedoen J.-C., Saito T., Averin S., Gissot S., Giordanengo B., Berger G., Kroth U., Jaeger J.-C., Gottwald A. Developments, characterization and proton irradiation damage tests of AlN detectors for VUV solar observations. Nuclear Instruments and Methods in Physics Research B , 2013 , B312. С. 48-53. ISSN 0168-583X

Полный текст не доступен из этого репозитория. (Заказать копию)

Аннотация

For next generation spaceborne solar ultraviolet radiometers, innovative metal–semiconductor–metal detectors based on wurtzite aluminum nitride are being developed and characterized. A set of measurement campaigns and proton irradiation damage tests was carried out to obtain their ultraviolet-to-visible characterization and degradation mechanisms. First results on large area prototypes up to 4.3 mm diameter are presented here. In the wavelength range of interest, this detector is reasonably sensitive and stable under brief irradiation with a negligible low dark current (3–6 pA/cm2). No significant degradation of the detector performance was observed after exposure to protons of 14.4 MeV energy, showing a good radiation tolerance up to fluences of 1 x 1011 protons/cm2.

Тип объекта:	Статья
Авторы на русском. ОБЯЗАТЕЛЬНО ДЛЯ АНГЛОЯЗЫЧНЫХ ПУБЛИКАЦИЙ!:	БенМоусса А., Солтани А.,Гербедон,Д.С., Саито Т.,Аверин С.,Гиссот С., Джорданенго Б., Бергер Г., Крот Ю., Ягер Д.С., Готтвальд А.
Подразделения (можно выбрать несколько, удерживая Ctrl):	257 лаб. быстропротекающих оптических явлений в твердотельных структурах
URI:	http://cplire.ru:8080/id/eprint/457

Только для зарегистрированных пользователей

Изменить объект