Balashov V V, Zakharov L.Yu., Inyushkin A.V., Kanaev A Yu, Kozlov A.B., Kozlova S.M., Koromyslov A L, Lopukhin K V, Luzanov V. A., Pervakov K.S., Tupitsyn I M, Chernodoubov D.A., Cheshev E A Comparative study of LuxY1-xAG (x=0..1) laser ceramics doped with 5% Yb3+. Ceramics International , 2022 , 48 (5). С. 6294-6301.
Это последняя версия данного объекта.
Аннотация
Materials with high thermo mechanical properties are required as laser media for high-powered lasers. One of such materials is lutetium-aluminum garnet (LuAG) doped with ytterbium. In the present work, we discuss for the first time a full comparative study of 5% Yb-doped LuYAG ceramics with variation Lu/Y ratio. Samples were prepared with addition of B2O3, MgO and SiO2 which were used as sintering aids. Grain sizes, shrinkage curves, lattice constants and transmission spectra were measured for all samples. Thermal conductivity was measured in a wide temperature range for all studied samples. Output power of 12 W and 60% slope efficiency were obtained on the 5% Yb:LuAG disk laser.
| Тип объекта: | Статья |
|---|---|
| Авторы на русском. ОБЯЗАТЕЛЬНО ДЛЯ АНГЛОЯЗЫЧНЫХ ПУБЛИКАЦИЙ!: | В.В. Балашов, Л.Ю. Заҳаров, A.В. Инюшкин, A.Ю. Канаев, A.Б. Козлов, С.М. Козлова, A.Л. Коромыслов, К.В. Лопуҳин, В.A. Лузанов, К.С. Перваков, И.М. Тупицын, Д.A. Чернодоубов, Е.A. Чешев |
| Подразделения (можно выбрать несколько, удерживая Ctrl): | 215 лаб. проблем субмикронной технологии 216 лаб. технологических процессов твердотельной электроники 218 лаб. химических методов технологии и анализа |
| URI: | http://cplire.ru:8080/id/eprint/9566 |
Доступные версии этого объекта
-
Comparative study of LuxY1-xAG (x=0..1) laser ceramics doped with 5% Yb3+. (deposited 24 Окт 2023 15:47)
- Comparative study of LuxY1-xAG (x=0..1) laser ceramics doped with 5% Yb3+. (deposited 30 Окт 2023 14:08) [В настоящее время Отображен]
 |
Изменить объект |