Fabrication of YAG:RE (RE = Yb, Nd, Cr) Ceramics Using Divalent Sintering Aids

Balashov V V, Kopylov Yu L, Kravchenko V B, Lopukhin K V, Shemet V V, Zakharov L Yu Fabrication of YAG:RE (RE = Yb, Nd, Cr) Ceramics Using Divalent Sintering Aids. In: Breakthrough directions of scientific research at MEPhI: Development prospects within the Strategic Academic Units. , р. 106.

Полный текст не доступен из этого репозитория.

Аннотация

High-quality YAG:RE (Yb, Nd, Cr) ceramics with CaO and MgO as sintering aids were manufactured by solid state reactive sintering method in vacuum. Influence of annealing temperature on optical properties was studied. This combination of sintering aids requires annealing temperatures at least 1300∘C to fully eliminate oxygen vacancies and at least 1400∘C to convert Cr3+ to Cr4+. It was found that annealing in oxidizing atmosphere creates strong changes in short wavelength transmittance.

Тип объекта:	Доклад на конференции или семинаре (Доклад)
Авторы на русском. ОБЯЗАТЕЛЬНО ДЛЯ АНГЛОЯЗЫЧНЫХ ПУБЛИКАЦИЙ!:	Балашов В.В., Копылов Ю.Л. Кравченко В.Б, Лопухин К.В, Шемет В.В., Захаров Л.Ю.
Подразделения (можно выбрать несколько, удерживая Ctrl):	215 лаб. проблем субмикронной технологии
URI:	http://cplire.ru:8080/id/eprint/8797

Доступные версии этого объекта

• Fabrication of YAG:RE (RE = Yb, Nd, Cr) Ceramics Using Divalent Sintering Aids. (deposited 24 Окт 2023 15:42) [В настоящее время Отображен]
  • Fabrication of YAG:RE (RE = Yb, Nd, Cr) Ceramics Using Divalent Sintering Aids. (deposited 26 Окт 2023 15:09)

Только для зарегистрированных пользователей

Изменить объект