Direct Measurements of Adiabatic Temperature Change in Ni49.9Mn37.03Sb12.3Fe0.77 Alloy due to Magnetocaloric Effect in the Temperature Range of Martensitic Transformation

Konoplyuk S. M., Mashirov A. V., Kamantsev A. P, Koledov V. V., Koshelev A. V., Shavrov V. G., Kokorin V. V. Direct Measurements of Adiabatic Temperature Change in Ni49.9Mn37.03Sb12.3Fe0.77 Alloy due to Magnetocaloric Effect in the Temperature Range of Martensitic Transformation. IEEE Transactions on Magnetics , 2018 , 54 (1). С. 1-4. ISSN 0018-9464

[img]
Предварительный просмотр
Текст
2018_Konoplyuk_IEEE.pdf

Загрузить (936kB) | Предварительный просмотр
Официальный URL: https://doi.org/10.1109/TMAG.2017.2761322

Аннотация

The magnetic and magnetocaloric measurements are reported for Ni49.9Mn37.03Sb12.3Fe0.77. The application of magnetic field was found to result in a shift of characteristic temperatures of the martensitic transformation (MT) by 0.7 K/T. Direct measurements of magnetocaloric effect (MCE) were employed to evaluate potential of this alloy for magnetic refrigeration. Peak values of MCE in magnetic field of 5 T were determined to be ~ -0.6 K in the interval of MT, and ~1 K in the vicinity of Curie temperature.

Тип объекта: Статья
Авторы на русском. ОБЯЗАТЕЛЬНО ДЛЯ АНГЛОЯЗЫЧНЫХ ПУБЛИКАЦИЙ!: Коноплюк С.М., Кокорин В.В., Маширов А.В., Каманцев А.П., Коледов В.В., Шавров В.Г., Кошелев А.В.
Подразделения (можно выбрать несколько, удерживая Ctrl): 192 лаб. магнитных явлений в микроэлектронике
URI: http://cplire.ru:8080/id/eprint/7256
Только для зарегистрированных пользователей
Изменить объект Изменить объект