Kholodkova Anastasia, Danchevskaya Marina, Popova Nellya, Pavlyukova Liana, Fionov Alexandr Preparation and dielectric properties of thermo-vaporous BaTiO3 ceramics. Materiali in Tehnologije , 2015 , 49 (3). С. 447-451. ISSN 1580-2949
Полный текст не доступен из этого репозитория.Аннотация
A crystalline BaTiO3 powder was synthesized at 350 °C for 0–20 h from TiO2 (> 99 % purity) and BaO (> 98 % purity) with water vapour acting as the reaction media. According to the XRD and SEM results, the BaTiO3 synthesized for 3 h proved to be the most adequate raw material for ferroelectric ceramics among the obtained samples as long as it consisted of pure crystalline sphere-shaped BaTiO3 particles with the average size of 156 nm. Pellets were pressed at (100, 150 and 200) MPa and sintered at 1300 °C for 1 h. The influence of the compacting pressure on the dielectric characteristics of BaTiO3 ceramics was studied by monitoring the permittivity and loss-tangent values of the pellets at 20 Hz–2 MHz. Kristalni prah BaTiO3 je bil sintetiziran pri 350 °C od 0 do 20 h iz TiO2 (~istost: > 99 %) in BaO (~istost: > 98 %) z vodno paro kot reakcijski medij. Iz rentgenogramov in SEM-posnetkov izhaja, da je BaTiO3, sintetiziran 3 h, najprimernej{a surovina med vsemi vzorci za feroelektri~no keramiko, dokler sestoji iz ~istih kristalnih okroglih delcev BaTiO3 s povpre~no velikostjo 156 nm. Peleti so bili stiskani pri (100, 150 in 200) MPa in sintrani 1 h pri temperaturi 1300 °C. Vpliv tlaka pri stiskanju na dielektri~ne lastnosti keramike BaTiO3 je bil preiskovana s spremljanjem permitivnosti in velikosti izgube tg d peletov pri 20 Hz–2 MHz. Klju~ne besede: barijev titanat, termo-parno porozna sinteza, mikrostruktura, dielektri~na keramika
| Тип объекта: | Статья |
|---|---|
| Авторы на русском. ОБЯЗАТЕЛЬНО ДЛЯ АНГЛОЯЗЫЧНЫХ ПУБЛИКАЦИЙ!: | Холодкова Анастасия, Данчевская Марина, Попова Нелли, Павлюкова Лиана, Фионов Александр |
| Подразделения (можно выбрать несколько, удерживая Ctrl): | 193 лаб. физических свойств нанокомпозитных материалов для информационных технологий |
| URI: | http://cplire.ru:8080/id/eprint/2643 |
 |
Изменить объект |